Made from BK7 material, which has transparent range from 330-2100nm. The refractive index is 1.5168 at 587.6nm. The BK7 window has good performance over visible and near IR spectrum for most application.
High Precision Achromatic Waveplate
Achromatic Waveplate Achromatic Waveplates(Retarders), AWP is composed of one piece of Crystal Quartz and one piece of Magnesium Fluoride, MgF2.
IR Windows Barium Fluoride BaF2 Window
Barium fluoride (BaF2) shows good optical transmission over UV-IR windows in 0.15μm~12.5μm.
IR Windows Magnesium Fluoride MgF2 Windows
MgF2 windows are used in the UV, visible and IR ranges, with approximately 94% transmission from 200 - 1000 nm, and approximately 95% transmission from 1-6µm
IR Windows Calcium fluoride CaF2 Windows
CaF2 has transparent range from 170-7800nm. The refractive index is 1.399 at 5000nm. 1. Low absorption coefficient 2. High damage threshold, 3. Low Dispersion (with an Abbe Number of 95) 4. Low fluorescence 5. Excellent water, chemical, and heat resistance

IR Lens

LOADING IMAGES

Zinc Selenide Lenses and Windows

Infrared Zinc Selenide Lenses, windows is for High-Power CO2 Lasers
Primary candidate for high-power CO2 Lasers windows
For windows, domes and lenses for full infrared region devices, especially for high resolution FLIR systems
1. Broadband AR Coating for the 7 - 12 μm Range
2. Compatible with Visible Alignment Lasers

product orgin:
China
shipping port:
Fuzhou China
payment:
T/T Payment, Western Union

inquiry now

features

Zinc Selenide Lenses and Windows

Infrared Zinc Selenide Lenses, windows is for High-Power CO2 Lasers
Primary candidate for high-power CO2 Lasers windows
For windows, domes and lenses for full infrared region devices, especially for high resolution FLIR systems
1. Broadband AR Coating for the 7 - 12 μm Range
2. Compatible with Visible Alignment Lasers

Parameters	CVD ZnSe
Homogeneity of refractive index	<1×10-5@10.6μm
Hardness(knoop)(kg/mm2)	105
Rupture modulus(Mpa)	55
Young's Modulus(GPa)	67.2
Posson ratio	0.28
Melting point	1520
Density, (g/cm3)	5.27
Thermal conductivity(W/cm.K)	0.18
Thermal expansion coefficient, (10-6 ，℃-1 )	5.75
Specific heat (Cal/g.k.)	0.086
Dielectric constant	8.98

Maximum size: Ø200×12mm

WTS make customized ZnSe Lenses, ZnSe windows, ZnS Lenses, ZnS windows

tags : Zinc Selenide Lenses Zinc Selenide Windows Infrared ZnSe Lenses Infrared ZnSe Windows ZnSe Lens For CO2 Laser Infrared ZnS Lenses

prev :
Germanium Infrared Lenses

Request a free quote

related products

Germanium Infrared Lenses
Germanium lenses are perfect for Mid-Infrared(IR) applications 1. Excellent for Security, Military, and Imaging Applications 2. AR Coating Optimized for the 7 - 12 µm Range
Triplet Achromatic Lenses
Hastings triplets achromatic lenses are designed to provide an infinite conjugate ratio and are useful for focusing collimated beams and for magnification. Steinheil triplets achromatic lenses are designed to provide a finite conjugate ratio and 1:1 imaging.
YAG Laser Crystal
YAG Laser Crystal, Un-doped YAG Crystal (pure YAG) Nd:YAG (Neodymium-doped yttrium aluminium garnet; Nd:Y3Al5O12) Yb:YAG(Ytterbium-doped yttrium aluminium garnet;Yb:Y3Al5O12) Cr4+:YAG(Chromium-doped yttrium aluminium garnet;Cr4+:Y3Al5O12) ER:YAG(Erbium-doped yttrium aluminium garnet;Er:Y3Al5O12)
IR Windows Magnesium Fluoride MgF2 Windows
MgF2 windows are used in the UV, visible and IR ranges, with approximately 94% transmission from 200 - 1000 nm, and approximately 95% transmission from 1-6µm
IR Windows Zinc Sulfide ZnS Windows
ZnS is used widely for IR components, windows and lenses, and applied for Thermal Imaging, long-wave infrared sensors.
Optical Brewster Mirror and Elliptical Shape Mirrors
Elliptical Shape Mirrors Made of by Fused Silica or N-BK7 Coated by Dielectric coating or metal (Al, Au, Ag)coating Shape could be customized