Made from BK7 material, which has transparent range from 330-2100nm. The refractive index is 1.5168 at 587.6nm. The BK7 window has good performance over visible and near IR spectrum for most application.
Achromatic Waveplate Achromatic Waveplates(Retarders), AWP is composed of one piece of Crystal Quartz and one piece of Magnesium Fluoride, MgF2.
Barium fluoride (BaF2) shows good optical transmission over UV-IR windows in 0.15μm~12.5μm.
MgF2 windows are used in the UV, visible and IR ranges, with approximately 94% transmission from 200 - 1000 nm, and approximately 95% transmission from 1-6µm
CaF2 has transparent range from 170-7800nm. The refractive index is 1.399 at 5000nm. 1. Low absorption coefficient 2. High damage threshold, 3. Low Dispersion (with an Abbe Number of 95) 4. Low fluorescence 5. Excellent water, chemical, and heat resistance
product orgin:
Chinashipping port:
Fuzhou Chinapayment:
T/T Payment, Western UnionKTP Nonlinear Crystals
KTP crystal (KTiOPO4) is mostly used as nonlinear crystals for frequency doubling of solid-state Nd:YAG crystal or Nd:YVO4 crystal laser, as it has large nonlinear optical coefficients, wide angular bandwidth and small walk-off angle, broad temperature and spectral bandwidth
KTP Crystal Advantages:
1. Large Nonlinear Optical (NLO) Coefficients
2. Wide Angular Bandwidth and Small Walk-off Angle
3. Broad Temperature and Spectral Bandwidth
4. High Electro-Optic (E-O) Coefficient and Low Dielectric Constant
5. Large Figure of Merit for an Optical Waveguide Modulator
6. Nonhygroscopic, Good Chemical and Mechanical Properties
KTP Crystal Applications:
1. Frequency Doubling (SHG) of Nd-doped Lasers for Green/Red Output.
2. Frequency Mixing (SFM) of Nd Laser and Diode Laser for Blue Output.
3. Parametric Sources (OPG, OPA and OPO) for 0.6mm-4.5mm Tunable Output.
4. E-O Modulators, Optical Switches, Directional Couplers.
5. Optical Waveguides for Integrated NLO and E-O Devices.
SPECIFICATION:
Aperture: 2x2 ~ 15x15mm
Lenght: 0.1 - 20mm
Cutting Angle: Determined by different kinds of homonic generartion
Phase matching type: Type I or Type II
End Configuration: Flat or Brewst or Specified
Angle tolerance: Δθ< ± 0.5°; Δφ< ±0.5°
Dimensional Tolerance: (W ± 0.1mm) x (H ± 0.1mm) x (L + 0.2mm/-0.1mm)
Flatness: <λ/8 at 633nm
Surface Quality: 10/5 Scracth/Dig
Parallelism: < 30 arc seconds
Perpendicularity: < 10 arc minutes
Wavefront Distortion: <λ/8 at 632.8nm
Clear Aperture: >90%
Chamfer: 0.15x45°
Coating:
a) S1,S2: AR @ 1064 nm R<0.1% & 532nm R<0.25%
b) S1:HR @ 1064nm R>99.8% & HT@ 808nm T>95%
S2:AR @ 1064 nm R<0.1% & 532nm R<0.25%
WTS Photonics owns strong production capability in our modern workshops, At present, we employ 150 staff, among whom one third are professionals taking the responsibility of R&D and directing the production practice.
If you want to custom KTP crystal,Coated KTP Windows,KTP Crystal Optics Products,etc. Welcome to contact our sales!
Retroreflectors (Corner Cube Prisms) reflect an image or beam back toward its original direction via three total internal reflections (TIR) 180° Reflection Inverts Image 3 arcsec Beam Deviation
Glued prisms are glued by different shape prisms. WTS offer Special Prisms like Half Penta Prisms, Pellin-Broca Prisms, Pechan Prisms etc. prisms
Survey Prisms are for Surveying or land surveying is the technique, profession, and science of determining the terrestrial or three-dimensional positions of points and the distances and angles between them.
Plaon-concave cylindrical lenses are used to provide focusing power in one section only, For illumination or detection of light from line sources.Also used for anamorphic compression of beams and images. 1. Ideal for Applications Requiring Magnification in One Dimension 2. Used to Transform a Collimated Beam into a Line 3. Rectangular and Circular 1
Germanium lenses are perfect for Mid-Infrared(IR) applications 1. Excellent for Security, Military, and Imaging Applications 2. AR Coating Optimized for the 7 - 12 µm Range
YAG Laser Crystal, Un-doped YAG Crystal (pure YAG) Nd:YAG (Neodymium-doped yttrium aluminium garnet; Nd:Y3Al5O12) Yb:YAG(Ytterbium-doped yttrium aluminium garnet;Yb:Y3Al5O12) Cr4+:YAG(Chromium-doped yttrium aluminium garnet;Cr4+:Y3Al5O12) ER:YAG(Erbium-doped yttrium aluminium garnet;Er:Y3Al5O12)